- Product categories
-
Multi-ply Fabric Conveyor Belt
Steel Cord Conveyor Belt
Heat Resistant Conveyor Belt
Flame Resistant Conveyor Belt
Pipe Conveyor Belt
Rough Top Conveyor Belt
Oil Resistant Conveyor Belt
Chevron Conveyor Belt
Side Wall Conveyor Belt
Cold Resistant Conveyor Belt
Bucket Elevator Conveyor Belt
Anti Acid and Alkakli Conveyor Belt
Solid Woven Conveyor Belt
Light PVC Conveyor Belt
Rip Stop Conveyor Belt
Rubber Track
Seal Belt
Cross Rigid Conveyor Belt
Straight Warp (SW) Conveyor Belt
Spiral Steel-cored Net (SN) Belt
Crows Foot Weave Fabric Belt
-
Your current location > Home > Product list- CONVEYOR BELTS - Oil Resistant Conveyor Belt - Oil Resistant Conveyor Belt
-
Product name：Oil Resistant Conveyor Belt 
-
Detailed description
Product features:
1、Oil resistant belt carries parts and components coated with machine oil, heavy-oil treated coal in cooking plants and electric power generating plants, soybean draff, fish meat and other oily materials. Materials containing non-polar organic solvents and fuel.
2､The belt compounded of oil resistant synthetic rubber has good resistance to the damaging effects encountered when conveying oil contaminated or treated materials.
3､Oil resistant conveyor belt can be divided into two types according to cover properties: Anti-abrasive type(D) and Ordinary type(L).
Technical data：
After the aging test(70℃*168h), at cover rubber rate of “tensile strength at breaking” and “elongation at breaking “,the value change is not over 25% than before.
Grade
Breaking Strength，Mpa
Elongation At Break，%
Abrasion，Mm3
L
≥14.0
≥350
≤200
Grade
Breaking Strength，Mpa
Elongation At Break，%
Abrasion，Mm3
L
≥14.0
≥350
≤200
D
≥16.0
≥350
≤160
Note：L----Under the general oil resistant condition；
D---Under the high abrasion and oil resistant condition
Item
Testing condition
Volume change rate，%
ASTM 471
Soak temperature，℃
soak time，h
L
D
1
IRM 901
70±2
70±1
+20
-5
2
IRM 902
70±2
70±
+50
+5
3
IRM 903
100±2
22±0.25
+50
+5
Note: when you test the oil resistant, choice one of oil in above is ok.
Technical data：
After the aging test(70℃*168h), at cover rubber rate of “tensile strength at breaking” and “elongation at breaking “,the value change is not over 25% than before.